• Remarkable improvement of anti-hydrolysis property
• Less pyrolysis gas emission and irritating smell during melt molding process
• Good weatherability

Grade	HMV-15CA	HMV-5CA-LC
Appearance	Granular	Granular
Ave.Diameter	≦1000µm	≦1000µm
Softening point*	158°F/70°C	149°F/65°C
5% weight loss temperature*	626°F/330°C	572°F/300°C
NCO%	0%	0%

*Standard Value

New Grade HMV-5CA-LC Characteristic

• Less viscosity increase during melt molding process
• Use of the CARBODILITE HMV-5CA-LC in Food package application as prepolymer of resin material according to EFSA(EU No.10/2011) is possible.

• PLA (Polylactic acid)
• PBS (Polybutylene succinate)
• PHA (Polyhydroxy alkanoic acid)
• Starch-based resin
• PET (Recycled PET, Bio PET)
• PBT (Polybutylene terephthalate)
• Polyester elastomer

All other polymers containing ester groups

• Automotive interior parts
• Chassis/ coverings of home electrical appliance
• Building decorative board
• Shopping bag
• Agricultural film
• Food container
• Covering material of cable
• Connector parts
• Toy and Stationery

• Hydrolysis stabilizer for polyesters including Biodegradable resin
• Hygrothermal Resistant Test
  Resin : PLA (Polylactic acid)
  Test condition : 176°F/80°C × 95%RH

• Hydrothermal Resistant Test
  Resin : PBS
  Test condition : 176°F/80°C × 95%RH

• Weatherability Test
  Resin : PLA (Polylactic acid)
  Test condition : Xenon, B.P.T. 145°F/63°C, 50%RH, 100W/m²

• Reduction of initial acid value
• Leaving non-reaction carbodiimide, and catch acid occurring over time

TSCA (USA)	Registered
REACH (EU)	Polymer (All materials is Registered)
KECI (KOREA)	Registered
IECSC (CHINA)	Registered
TCSI (TAIWAN)	Registered
ENCS (JAPAN)	Registered

Please ask us the detail of this inventory because it depends on the grades.